ACE-ZNS20-C, ACE-ZNS 20 C · zinc stearate, wood coating grade. 3,000 kg planned, started 22 May 2026, due 24 May 2026, operator Malcolm Rees.
Materials issued
$9,723
3 components out of 1310
Labour & plant recovered
$2,394
9.2 hours across 3 work centres
Overhead applied
$1,005
42% of recovery
Carried in 1320 WIP
$13,122
$4.47/kg made
Formulation Rev 4 approved 08 Oct 2025 by Amir Haddad
Issued against this works order, with the supplier lot recorded on every line, which is the backward half of a trace.
| Raw material | kg / tonne | Required | Lot | Cost /kg | Value |
|---|---|---|---|---|---|
| RM-1010 Stearic acid, triple pressed, vegetable | 748 | 2,244 | KLK-2404500 | $2.48 | $5,565 |
| RM-2022 Zinc oxide, active, high surface area · Active ZnO, wood coating fineness | 238 | 714 | ZIB-2609960 | $5.62 | $4,013 |
| RM-6040 Precipitated silica, anti-caking | 14 | 42 | SIB-2504817 | $3.46 | $145 |
| Material cost | $9,723 | ||||
Routing
Each step recovers its work centre's rate for the hours run, and overhead is applied on top. That is the conversion cost inside WIP.
| Seq | Work centre | Operation | Hours | Rate /hr | Recovered |
|---|---|---|---|---|---|
| 10 | RX-01 Reaction Vessel 1 (fusion) | Direct fusion with stearic acid at 135°C | 3.3 | $380.00 | $1,254 |
| 20 | DR-02 Flash Dryer | Flash dry and cool | 4.8 | $195.00 | $936 |
| 30 | PK-01 Packing Line (20 kg sacks & 500 kg FIBC) | Pack to 500 kg FIBC / 20 kg sack | 1.1 | $185.00 | $204 |
Quality release · Metallic stearate release
Recorded 24 May 2026 by Vinh Le. Precipitated and fused stearates. Metal content and sieve residue decide the grade.
| Test | Result | Specification | Outcome |
|---|---|---|---|
| Yield | 99.21 % | 97.5-100 % | Within spec |
| Peak temperature | 133.7 °C | 128-142 °C | Within spec |
| Metal content | 6.83 % | 6.2-7.4 % | Within spec |
| Moisture | 0.48 % | 0-1.5 % | Within spec |
| Bulk density | 315 g/L | 260-400 g/L | Within spec |
| Sieve residue 75 µm | 0.02 % | 0-0.5 % | Within spec |
| Melting point | 157.4 °C | 145-165 °C | Within spec |
| Free fatty acid | 0.50 % | 0-1.2 % | Within spec |
Standard cost
Computed from the formulation and the routing, not typed in. It is what the finished goods control account is debited at.
- Material /kg
- $3.24
- Conversion /kg
- $1.13
- Standard /kg
- $4.37
- List /kg
- $7.35
- Margin at list
- 40.5%
Yield
- Planned
- 3,000 kg
- Made
- 2,936 kg
- Formulation standard
- 98.3%
- Actual
- 97.87%
- Variance to 5400
- $292
Released as batch B26-0273
2,936 kg made, 475 kg still on the floor at the Main Store. Best before 22 May 2028.
Full trace →Ledger effect
DR 1320 Work in Process Control, as material is issued and hours are booked
CR 1310 Raw Materials Control
DR 1330 Finished Goods Control, on a quality release, at standard
DR/CR 5400 Yield Variance, the difference
DR 1350 Quarantined Stock, on a failure, instead of 1330
Each line posts at the moment of the transaction it belongs to.
SUNACE
Australia · Leading through quality
Sun Ace Australia Pty Ltd
32-38 Remington Drive, Dandenong South VIC 3175
ABN 52 006 388 102 · +61 3 9702 9444 · sunace@sunace.com.au
Batch manufacturing record
WO-2026-0273
- Grade
- ACE-ZNS20-C
- Batch
- B26-0273
- Made
- 23 May 2026
| Raw material | Lot | kg issued | Cost |
|---|---|---|---|
| RM-1010, Stearic acid, triple pressed, vegetable | KLK-2404500 | 2,244 | $5,565 |
| RM-2022, Zinc oxide, active, high surface area | ZIB-2609960 | 714 | $4,013 |
| RM-6040, Precipitated silica, anti-caking | SIB-2504817 | 42 | $145 |
| Quality test | Result | Specification |
|---|---|---|
| Yield | 99.21 % | 97.5-100 |
| Peak temperature | 133.7 °C | 128-142 |
| Metal content | 6.83 % | 6.2-7.4 |
| Moisture | 0.48 % | 0-1.5 |
| Bulk density | 315 g/L | 260-400 |
| Sieve residue 75 µm | 0.02 % | 0-0.5 |
| Melting point | 157.4 °C | 145-165 |
| Free fatty acid | 0.50 % | 0-1.2 |
Manufactured by Malcolm Rees
Released by Quality Manager