B26-0295
Pass Main StoreACE-ZNS20-C, ACE-ZNS 20 C · zinc stearate, wood coating grade. 2,924 kg made on 21 May 2026 against WO-2026-0295, 201 kg still on the floor, best before 20 May 2028.
← Backward trace
Every raw material lot consumed into this batch, and the supplier it came from. If a supplier recalls a lot, this is the list of batches it touched.
| Raw material | Supplier lot | Supplier | kg |
|---|---|---|---|
| RM-1010 Stearic acid, triple pressed, vegetable | KLK-2407665 | KLK OLEO (Malaysia) Sdn Bhd | 2,244 |
| RM-2022 Zinc oxide, active, high surface area | ZIB-2601424 | Zibo Xiangrun Chemical Co. Ltd | 714 |
| RM-6040 Precipitated silica, anti-caking | SIB-2405264 | Sibelco Australia Ltd | 42 |
| Charged into the batch | 3,000 kg | ||
Forward trace →
Every despatch this batch went out on. If a customer raises a complaint against a batch number, this is who else received it.
| Sales order | Customer | Despatched | kg |
|---|---|---|---|
| SO-00711 | Akzo Nobel Pty Ltd Sunshine VIC | 31 Aug 2025 | 1,798 |
| SO-01038 | Haymes Paint Pty Ltd Ballarat VIC | 22 Jul 2026 | 504 |
| SO-00914 | Haymes Paint Pty Ltd Ballarat VIC | 13 Mar 2026 | 260 |
| Despatched · remaining | 2,562 · 201 kg | ||
Release record · Metallic stearate release
Tested 22 May 2026 by Vinh Le. Precipitated and fused stearates. Metal content and sieve residue decide the grade.
SUNACE
Australia · Leading through quality
Sun Ace Australia Pty Ltd
32-38 Remington Drive, Dandenong South VIC 3175
ABN 52 006 388 102 · +61 3 9702 9444 · sunace@sunace.com.au
Certificate of analysis
B26-0295
- Grade
- ACE-ZNS20-C
- Manufactured
- 21 May 2026
- Best before
- 20 May 2028
- Quantity
- 2,924 kg
Sun Ace Australia Pty Ltd certifies that batch B26-0295 of ACE-ZNS20-C, ACE-ZNS 20 C · zinc stearate, wood coating grade, was manufactured at Dandenong South under our ISO 9001:2015 quality system and tested against quality plan QP-STEARATE (Metallic stearate release) with the following results.
| Test | Result | Specification | Method |
|---|---|---|---|
| Yield | 99.63 % | 97.5-100 % | SA-QC-YIEL |
| Peak temperature | 134.9 °C | 128-142 °C | SA-QC-TEMP |
| Metal content | 6.80 % | 6.2-7.4 % | SA-QC-META |
| Moisture | 0.61 % | 0-1.5 % | SA-QC-MOIS |
| Bulk density | 303 g/L | 260-400 g/L | SA-QC-BULK |
| Sieve residue 75 µm | 0.07 % | 0-0.5 % | SA-QC-SIEV |
| Melting point | 155.7 °C | 145-165 °C | SA-QC-MP |
| Free fatty acid | 0.34 % | 0-1.2 % | SA-QC-FFA |
Metallic stearate grades are produced from vegetable-based fatty acids and are declared free of animal substances and BSE free. A retained sample is held for 24 months from the date of manufacture. Handle in accordance with the current safety data sheet.
Released by Vinh Le